实验报告姓名:骆涛学号:PB06210288系别:0611座号:12实验题目:通过霍尔效应测量磁场实验目的:通过实验测量半导体材料的霍尔系数和电导率可以判断材料的导电类型、载流子浓度、载流子迁移率等主要参数实验内容:已知参数：b=4.0mm,d=0.5mm,=3.0mm.设，其中K=6200GS/A；1.保持=0.450A不变，测绘曲线测量当正(反)向时,正向和反向时的值,如下表调节控制电流/mA0.51.01.52.02.53.03.54.04.5正向B正向/mV-1.76-3.52-5.26-7.02-8.75-10.50-12.27-14.01-15.75B反向/mV1.823.665.467.309.0910.9112.7414.5416.35反向B反向/mV-1.82-3.66-5.46-7.29-9.08-10.90-12.74-14.54-16.35B反向/mV1.753.525.267.038.7510.5012.2714.0115.75绝对值平均值/mV1.793.595.367.168.9210.7012.5014.2716.05做出曲线如下1由origin得由和得2.保持=4.50mA不变，测绘曲线测量当正(反)向时,正向和反向时的值,如下表调节励磁电流/A0.050.100.150.200.250.300.350.400.45正B正向/mV-1.48-3.22-5.01-6.79-8.57-10.33-12.14-13.95-15.74B反向/mV2.033.795.597.389.1710.9312.7414.5516.34反B反向/mV-2.03-3.79-5.59-7.38-9.17-10.92-12.74-14.55-16.33B反向/mV1.483.225.016.798.5710.3312.1413.9515.74绝对值平均值/mV1.763.515.307.088.8710.6312.4414.2516.04做出曲线如下2LinearRegressionforData1_V:Y=A+B*XParameterValueError-------------------------------------------A0.017140.00789B3.564050.00313-------------------------------------------RSDNP--------------------------------------------10.010138<0.0001--------------------------------------------由origin得由和得3.在零磁场下，取=0.1mA，在正向和反向时，测量正向反向/mV8.72-8.69的绝对值平均值为=8.705mV4.确定样品的导电类型，并求、n、σ和μ(1)确定样品的导电类型3LinearRegressionforData3_V:Y=A+B*XParameterValueError-----------------------------------------A-0.055280.01437B35.723330.05109-----------------------------------------RSDNP-----------------------------------------0.999990.019799<0.0001------------------------------------------------------------控制电流和磁场方向如图所示时，电压表读数为正.可知薄片S的上表面积累正电荷,下表面积累负电荷.再根据洛沦兹力的受力规则判断,载流子受力向下,再由下表面积累负电荷知,载流子为负电荷.所以导电类型为n型.(2)求由1和2知，...