2007年5月农业机械学报第38卷第5期苎麻茎秆木质部力学性能试验3苏工兵刘俭英王树才黄钺文友先【摘要】以苎麻茎秆木质部为试验对象,在RGT-10型微机控制电子万能试验机上进行了弯折、拉伸、压缩试验。试验结果表明:“华苎4号”木质部的抗弯弹性模量为7358169MPa,最大抗弯强度为40177MPa;拉伸弹性模量为177126MPa,最大抗拉强度为32125MPa;压缩弹性模量为7170MPa。相同部位木质部的抗弯弹性模量明显高于拉伸弹性模量,最大抗弯强度大于最大抗拉强度,木质部横向抵抗变形能力强。拉伸弹性模量与压缩弹性模量有明显差异,木质部属各向异性材料,建立力学模型应采用各向异性的本构关系。关键词:苎麻茎秆木质部力学性质试验中图分类号:S56311;TB301文献标识码:AStudyonMechanicalPropertiesofXylemofRamieStalkSuGongbing1LiuJianying1WangShucai1HuangYue2WenYouxian1(1.HuazhongAgriculturalUniversity2.HubeiAcademyofAgriculturalSciences)AbstractThebending,tensileandcompressiveexperimentsoframiexylemofthevariety“Huazhu-4”wereconductedbyusinganuniversaltestingmachine“RGT-10”.Theresultsareasfollows:forramie“Huazhu-4”,theaveragebendingmodulusandstrengthofxylemare7358169MPaand40177MPa,respectively;anditsYong’smodulusandtensilestrengthare177126MPaand32125MPa,respectively.Itsaveragecompressivemodulusis7170MPaandbendingmodulusandstrengtharegreaterthanitsYong’smodulusandtensilestrength.Thereisadistinctdiffer2encebetweentensileandcompressivemodulus.Xylemisakindofanisotropicmaterialandmod2elingitsmechanicalmodelneedsanisotropicconstitutiverelations.KeywordsRamie,Stalk,Xylem,Mechanicalproperties,Experiment收稿日期:2006-11-233华中农业大学科技创新基金项目(项目编号:52207-07002)苏工兵华中农业大学工程技术学院高级工程师博士生,430070武汉市刘俭英华中农业大学工程技术学院副教授王树才华中农业大学工程技术学院副教授博士黄钺湖北省农业科学院经济作物所农艺师,430064武汉市文友先华中农业大学工程技术学院教授博士生导师引言剥麻是苎麻收获的关键环节,一直是制约我国苎麻生产效益提高和苎麻纺织品质量提升的“瓶颈”[1]。机械剥制方法是将茎秆木质部击碎,然后将韧皮纤维与木质部分离。由于缺乏对苎麻茎秆木质部力学性质试验研究,机械剥制主要工作部件的参数选择与设计没有可靠理论依据,仅...