第49卷Vol.49doi:10.3969/j.issn.1003-4226.2023.04.007第4期No.4金属制品MetalProducts55SiCr弹簧钢丝冷卷断裂原因分析2023年8月August2023郭晓霞，李志豪，张立良，李绍杰，蔡振雷，相楠（石家庄钢铁有限责任公司，河北石家庄050100）摘要：55SiCr弹簧钢丝在冷卷过程中发生断裂。观察断裂位置的宏观和微观形貌，并对断裂试样进行了化学成分、硬度、晶粒度以及金相组织分析。结果表明：悬架弹簧在冷卷过程中发生断裂，宏观观察断裂起源于弹簧外侧表面，弹簧试样表面存在横向擦伤，钢丝冷卷时产生应力集中是其断裂的主要原因。关键词：55SiCr；化学成分；断裂；应力集中；晶粒度中图分类号：TG356.4Causeanalysisoncoldrollfractureof55SiCrspringsteelwireGuoXiaoxia,LiZhihao,ZhangLiliang,LiShaojie,CaiZhenlei,XiangNan(ShijiazhuangIron&SteelCo.,Ltd.,Shijiazhuang050100,China)Abstract:55SiCrspringsteelwirefracturedduringcoldrollingprocess.Macroscopicandmicroscopicmorphologyoffrac-turelocationisobserved,andchemicalcomposition,hardness,grainsize,andmicrostructureoffracturesampleisana-lyzed.Resultsshowthatsuspensionspringfracturedduringcoldrollingprocess.Springfractureoriginatesfromoutersur-face,andtherearetransversescratchesonsurfaceofspringsample.Themainreasonforfractureisstressconcentrationgeneratedduringwirecoldrolling.Keywords:55SiCr;chemicalcomposition;fracture;stressconcentration;grainsize014mm规格55SiCr线材用于生产悬架弹簧钢丝,用户在钢丝冷卷过程中发现有产品发生断裂,影响生产效率。笔者从55SiCr冷卷断裂试样表面缺陷位置进行取样,利用金相显微镜和扫描电镜分析等方法,结合钢丝生产工艺流程，查找冷卷断裂试样产生缺陷的原因并进行分析。1宏观形貌分析悬架弹簧加工工艺：014mm线材放线→拉拔（012.5mm,冷拔1道）→淬火→回火一→收卷→开文献标识码：A卷一冷卷一→去应力回火一→喷涂。回火弹簧钢丝在冷卷悬架弹簧过程中断裂,55SiCr悬架弹簧断裂宏观形貌如图1所示。断裂起源于悬架弹簧表面，呈放射状扩展。断裂发生在第7圈，起源于弹簧外侧。2断裂原因分析2.1化学成分在断裂弹簧上取样，通过火花直读光谱仪分析化学成分,55SiCr断裂弹簧化学成分见表1。从表1(a)断裂弹簧图155SiCr悬架弹簧断裂宏观形貌Fig.1Macroscopicmorphologyof55SiCrsuspensionspringfracture（b）断裂位置宏...