混凝土早期收缩、开裂对结构耐久性的影响XXX1XXX1XXX2摘要由于早强水泥和高效减水剂广泛应用，混凝土凝固和硬化强度开展迅速，初期收缩变形受约束产生很大的弹性拉应力得不到松弛那么产生开裂，严重地影响处于侵蚀性环境混凝土结构的耐久性和安全性，迫切需要提高对这一问题的认识，并落实到设计、施工、材料各方面，使混凝土结构根底设施建设在新世纪能够可持续地开展。关键词早期混凝土自收缩开裂性能耐久性ShrinkageandCrackingofConcreteandItsEffectonDurabilityofStructuresQuTao1LuoJianFeng2(1.WuhanuniversityoftechnologyWuhan4300702.TongjiuniversityShanghai202392)AbstractConcretehasbeensetandhardenedfastanditsstrengthdevelopedquicklybecauseofapplicationofhighearlystrengthcementandsuperplasticizer,somaybecrackedsincedrasticelasticstressdevelopedandalmostnorelaxationeffectoccurredwhenshrinkswasrestrictedatearlyage.Itaffectsseriouslydurabilityandsafetyofconcretestructuresinaggressiveenvironment.Itisonedgetoimprovetheknowledgeinthisfield,toputintoeffectofdesign,constructionandmaterial.Theywouldplayanimportantruletosustainabledevelopmentofinfrastructureconstructioninthisnewcentury.Keywordshighearly-strengthconcrete,autogenousshrinkage,crackperformance,durability1.概述人们很早就已经认识到温度对混凝土开裂的影响，提出了掺入火山灰、采用低热水泥、利用大粗骨料粒径、预冷拌和物原材料、限制浇注层高和冷却水管等措施，来可降低水化温峰，抑制温度裂缝。但是，许多混凝土结构，包括桥梁、道路、隧道、港口、大坝、建筑物等，在建期间或建成后不长时间后出现可见裂缝，影响结构耐久性的现象还是十分严重。特别是近些年来随着早强混凝土的广泛应用，混凝土结构劣化迅速的情况越来越多。为什么会造成这种现象呢？因为很多人都无视了混凝土自身收缩的影响。自身收缩还会与混凝土温度收缩相叠加使很多断面并不大的构件产生裂缝。在混凝土硬化初期，其温度变形和自生变形是产生内应力，造成混凝土开裂的重要驱动力[1]。在拆模后，枯燥收缩变形进一步加剧了混凝土内应力的积累。混凝土的温度变形主要由其硬化期间的温度历程和热膨胀系数所决定[1]。混凝土的热膨胀系数是随着水泥水化进程而不断发生变化的，尤其在水化初期，混凝土的热膨胀系数变化显著。20×106/℃使用今活性高、粉磨细...